Hydrogen storage material

ABSTRACT

An economical metallic material for storage of hydrogen constituted by an intermetallic compound which exists as a Laves phase, has a hexagonal crystal structure of the MgZn 2  type (C14 type), and in which the crystal lattice parameters a and c are in the ranges a= 4.80˜ 5.10 (A) and c= 7.88˜ 8.28 (A). The material of the inventon permits absorption of large amounts of hydrogen and efficient desorption thereof under close to normal temperature and pressure conditions, and for reduced cost of material preferably includes as principal components manganese and at least titanium or zirconium.

The present invention relates to material for storage, preservation and transport of hydrogen.

It is known that in certain conditions of temperature and pressure of gaseous vapour, metals such as the transition elements of Groups III ˜ V of the periodic table may keep, absorb or combine chemically with hydrogen in high density to form metal hydrides, for example, LaH₃, CeH₃, TiH₂, ZrH₂, VH, and NbH, in which there is a maximum of three hydrogen atoms to one atom of the metal, and that when temperature and pressure conditions are subsequently changed in a specific manner absorbed hydrogen is released from these hydrides. Thus, hydrogen may be stored under safer conditions and may be transported more easily than is possible using conventional hydrogen cylinders, and may be made available as a gas when required. However, in comparison with a conventional hydrogen storage method in pressure vessels use of these substances has the disadvantage that comparatively extreme ambient conditions must be achieved in order to effect absorption and desorption of hydrogen thereby, since the substances form comparatively strong bonds with hydrogen. For example, if titanium is employed, when the pressure is in the vicinity of normal pressure, the metal must be heated to approximately 400° C. to permit effective absorption of hydrogen to proceed and must be heated to approximately 600° C. to cause subsequent desorption of hydrogen. The requirement for such high temperatures is of course disadvantageous from the viewpoint of fuel costs and also from the viewpoint of necessary equipment, particularly at distribution terminals where the hydrogen is employed. To overcome this disadvantage, a variety of other metallic materials for storing hydrogen have been proposed, typical examples being titanium or zirconium alloys such as FeTi, Ti (or Zr) -- Cu alloys, Ti (or Zr) -- Ni alloys and Ti (or Zr) -- Co alloys, magnesium alloys such as Mg₂ Cu and Mg₂ Ni, and rare earth compounds such as LaNi₅.

Of these materials, the magnesium alloys for example, permit storage of a comparatively large amount of hydrogen per unit weight of storage material. However, when magnesium alloys are employed, considerable energy must be supplied to effect desorption of stored hydrogen, since the dissociation pressure at room temperature is very low, and desorption of hydrogen can be effected only under conditions of high temperature exceeding 250° C., and even under these conditions it takes a long time and needs a large amount of energy. In contrast to this, the dissociation pressure of hydrogen stored in rare earth compounds is several atmospheres at room temperature, and both absorption and desorption of hydrogen can therefore be effected efficiently and comparatively rapidly at room temperature. On the other hand, the amount of storable hydrogen per unit weight of storage material is slightly less than that for other types of storage material, in addition to which there is of course the disadvantage from the viewpoint of large-scale use that rare earth materials are extremely expensive. Of the titanium alloys, the material which has been considered to be most promising is ferro-titanium, FeTi alloy, which has the advantages that it is comparatively cheap, that the dissociation pressure of hydrogen combined therewith is several atmospheres at room temperature, and that qualities of the material remain substantially unchanged after repeated absorption and desorption of hydrogen thereby. However, FeTi alloy also has disadvantages, in that a high temperature of over about 350° C. and high pressure of over about 30 atmospheres are necessary for initial hydriding thereof, that the rates of absorption and desorption of hydrogen thereby are comparatively slow, and that there is a certain amount of hysteris effect in the hydrogen absorption and desorption cycle effected therein, i.e., it is difficult to effect discharge of the complete amount of hydrogen absorbed by the material.

It is accordingly a principal object of the invention to provide improved hydrogen storage material in which the dissociation pressure of combined hydrogen is several atmospheres at room temperature, which is able to absorb and desorb hydrogen at high rates in normal temperature conditions, and which is of comparatively low cost, whereby said material is of great practical application.

It is a further object of the invention to provide hydrogen storage material which is suitable for employment by being enclosed in a pressure container for storage, preservation and transport of hydrogen gas.

According to the present invention, there is provided metallic material for storage of hydrogen which includes a substance able to store hydrogen and defining an alloy phase which is substantially a Laves phase constituted by an intermetallic compound, which has a hexagonal crystal structure of the MgZn₂ type (C14), and the crystal lattice parameters a and c of which have values in the ranges;

    a = 4.80 ˜ 5.10 (A),

    c = 7.88 ˜ 8.28 (A).

in a preferred embodiments of the present invention, said substance of metallic material able to store hydrogen is constituted substantially by an alloy phase including titanium and manganese, is constituted substantially by an alloy phase including zirconium and manganese, is constituted substantially by an alloy phase including titanium, zirconium, and manganese, or is constituted substantially by a Ti -- Zr -- Mn alloy, Ti -- Zr -- Mn -- Mo alloy or Ti -- Zr -- Mn -- Cu alloy.

The many advantages achieved by use of the material of the invention may be appreciated from the following detailed description of several preferred embodiments thereof when read in reference to the attached drawings, in which

FIG. 1 is a graph showing the relationship between the parameters a and c of unit cells in the crystal lattice of various hydrogen storage materials according to the invention, the preferred range of values of these parameters being indicated by the shaded portion of the drawing;

FIG. 2 is a ternary equilibrium diagram of the Ti -- Zr -- Mn alloy system in which the shaded portion indicates the range of alloys having outstanding qualities as hydrogen storage material;

FIG. 3 is a graph which plots hydrogen dissociation pressure -- composition isotherms for the Ti₀.5 Zr₀.5 Mn₂.0 -- H system by way of example of hydriding characteristics of a Ti -- Zr -- Mn alloy according to the invention;

FIG. 4 is a graph which plots the amount of initial hydrogen absorption at room temperature by an alloy having the formula Ti₁₋α Zr.sub.α Mn₂.0, having a crystal lattice of the MgZn₂ type, and existing in the Laves phase against the crystal lattice parameter a of the alloy;

FIG. 5 is a graph similar to the graph of FIG. 4 which plots the amount of initial hydrogen absorption against the crystal lattice parameter c;

FIG. 6 is a graph which plots the relationship of the amount of released hydrogen (cc/g) at room temperature to the value of y in a compound having the general formula Ti_(1-y) Zr_(y) Mn₁.9 Mo₀.1 by way of illustration of properties of another embodiment of the invention constituted by a Ti -- Zr -- Mn -- Mo alloy;

FIG. 7 is a similar drawing showing the relationship of the amount of released hydrogen (cc/g) at room temperature to the value of z in a compound having the general formula Ti₀.8 Zr₀.2 Mn_(2-z) Mo_(z) ;

FIG. 8 is a graph which plots equilibrium pressure -- composition isotherms for the system Ti₀.8 Zr₀.2 Mn₁.7 Mo₀.3 -- H by way of example of the hydriding characteristics of a Ti -- Zr -- Mn -- Mo alloy according to the invention;

FIG. 9 is a similar drawing which plots equilibrium pressure -- composition isotherms for the system Ti₁.7 Zr₀.3 Mn₁.9 Mo₀.1 -- H;

FIG. 10 is a graph showing the relation of the amount of released hydrogen (cc/g) at 60° C. to the value of y in an alloy having the general formula Ti_(1-y) Zr_(y) Mn₁.9 Cu₀.1 by way of illustration of another embodiment of the invention constituted by a Ti -- Zr -- Mn -- Cu alloy;

FIG. 11 is a similar drawing showing the relation of the amount of released hydrogen (cc/g) at 60° C. to the value of z in an alloy having the general formula Ti₀.7 Zr₀.3 Mn_(2-z) Cu_(z) ; and

FIG. 12 is a graph which plots equilibrium pressure -- composition isotherms for the system Ti₀.6 Zr₀.4 Mn₁.9 Cu₀.1 -- H in illustration of the hydriding characteristics of a Ti -- Zr -- Mn -- Cu alloy according to the invention.

The metallic material for storage of hydrogen according to the present invention is an intermetallic compound which exists effectively as a Laves phase, which has a hexagonal crystal structure of the MgZn₂ type (C14 type), and in which the values of the parameters a and c of a unit cell thereof are in the following ranges:

    a = 4.80 ˜ 5.10 (A)

    c = 7.88 ˜ 8.28 (A).

The metallic material for storage of hydrogen according to the invention forms a hydride in a short time at room temperature, i.e., in the vicinity of 20° C., absorbs and effects stable retention of a large amount of hydrogen in solid solution, and can be caused to release the hydrogen held thereby, even at room temperature, by lowering of ambient pressure to values lower than the characteristic values of dissociation pressure of hydrogen with respect to the various component substances constituting the material of the invention.

Analysis of the material of the invention by X-ray and similar techniques showed that with respect to composition the material is effectively an intermetallic compound existing in the Laves phase, and that its crystal structure is the MgZn₂ type (C14 type) belonging to the hexagonal system or of the MgCu₂ type (C15 type) belonging to the cubic system. Tests showed that material of having a crystal structure of the MgZn₂ type has particular advantages with respect to storage of hydrogen.

Typical examples of possible values of the crystal lattice parameters a and c of a compound having an MgZn₂ type (C14) crystal structure and existing as a Laves phase are shown in Table 1, which lists values given by Dr. Max Hansen in `Constitution of Binary Alloys` (1958).

                  Table 1                                                          ______________________________________                                         Compound       a.sub.0 (A)  c.sub.0 (A)                                        ______________________________________                                         MgZn.sub.2     5.22         8.557                                              BaMg.sub.2     6.649        10.676                                             CaCd.sub.2     5.993        9.654                                              CaLi.sub.2     6.26         10.25                                              CaMg.sub.2     6.23         10.12                                              CrBe.sub.2     4.27         6.92                                               FeBe.sub.2     4.212        6.853                                              KNa.sub.2      7.50         12.30                                              MnBe.sub.2     4.240        6.924                                              NbFe.sub.2     4.830        7.882                                              NbMn.sub.2     4.879        7.902                                              ReBe.sub.2     4.354        7.101                                              SrMg.sub.2     6.439        10.494                                             TaFe.sub.2     4.827        7.838                                              TaMn.sub.2     4.87         7.95                                               TiFe.sub.2     4.779        7.761                                              TiMn.sub.2     4.825        7.917                                              TiCr.sub.2     4.932        7.961                                              UNi.sub.2      4.966        8.252                                              VBe.sub.2      4.394        7.144                                              WBe.sub.2      4.446        7.289                                              WFe.sub.2      4.727        7.704                                              ZrCr.sub.2     5.102        8.238                                              ZrMn.sub.2     5.019        8.249                                              ZrRe.sub.2     5.262        8.593                                              ZrRu.sub.2     5.141        8.507                                              ZrOs.sub.2     5.189        8.526                                              ZrV.sub.2      5.288        8.664                                              ______________________________________                                    

An alloy having excellent properties as a hydrogen storage material is constituted by those binary alloys of Table 1, or by those ternary or quaternary alloys constituted by suitable combinations of the alloys of Table 1, whose alloy phase is substantially uniform, which crystallize well, whose crystal structure is of the MgZn₂ type existing in the Laves phase, and in which the a and c parameters of the crystal lattice are in the ranges; a = 4.80 ˜ 5.10 (A) and c = 7.88 ˜ 8.28 (A). If these conditions are met, a hydrogen storage material of similar high quality is obtained according to the invention by employing one or more of the alloys of Table 1 as a base material and forming an alloy by partial substitution of the base material with third, fourth, fifth, or further elements.

A study of the relation between the lattice parameters and hydrogen dissociation equilibrium pressure showed that dissociation pressure tends to increase as the lattice parameters become smaller. Considering the relation between this change of hydrogen dissociation pressure and the heat of formation of hydrides of Ti-Mn alloys it is found that whereas the heat of dissociation of hydrogen has a comparatively high negative value for titanium, which is in Group IVa of the periodic table, for manganese, which is in Group VIa, and for other elements of Groups VIa ˜ VIII other than palladium, Pd, the heat of formation of the hydride is positive, and that for palladium the heat of formation has a comparatively small negative value. In other words, the heat of formation of hydride in a Ti-Mn alloy can be made correspondingly small by increasing the proportion of the Mn component, and it is inferrable from this that reduction of hydrogen dissociation pressure may be achieved by increasing the proportion of the Ti component in a Ti-Mn alloy, since this increase is accompanied by an increase in the heat of formation of a hydride of the alloy and production of a more stable hydride.

Examples of alloys produced on the basis of these considerations, the values of the lattice parameters a and c of these alloys, and the amount of hydrogen absorbed thereby at room temperature, i.e., at approximately 20° C., are shown in Table 2, the amount of absorbed hydrogen being indicated as cubic centimeters per gram of alloy.

As indicated in Table 2, metallic material for hydrogen storage according to the invention principally includes titanium or zirconium, which are comparatively cheap and have large hydrogen storage capacity, and manganese, which is cheap and easily available.

FIG. 1 is a graph of the values of the crystal lattice parameters a and c of alloys according to the invention which are listed in Table 2. In the drawing the letters A ˜ W indicate the correspondingly identified alloys of Table 2, and the shaded portion indicates the range of materials presently claimed.

                  Table 2                                                          ______________________________________                                                                             Hydrogen                                                                       absorption                                                                     (cc/g)                                                                         at room temp.                                                                  (approx.)                                  Code Alloy Composition                                                                               a (A)   c (A) 20° C.)                             ______________________________________                                         A    TiMn.sub.1.0     4.925   8.085 283                                        B    TiMn.sub.1.28    4.891   7.962 216                                        C    TiMn.sub.2.0     4.818   7.902 8.2                                        D    TiCr.sub.2.0     4.904   7.979 104                                        E    ZrCr.sub.2.0     5.084   8.255 236                                        F    ZrMn.sub.2.0     5.040   8.274 215                                        G    Ti.sub.0.7 Zr.sub.0.3 Cr.sub.2.0                                                                4.973   8.038 202                                        H    TiMn.sub.0.8 Ce.sub.0.2                                                                         4.962   7.785 318                                        I    Ti.sub.0.2 Zr.sub.0.8 Mn.sub.2.0                                                                5.001   8.226 222                                        J    Ti.sub.0.5 Zr.sub.0.5 Mn.sub.2.0                                                                4.946   8.130 226                                        K    Ti.sub.0.7 Zr.sub.0.3 Mn.sub.2.0                                                                4.878   8.032 122                                        L    Ti.sub.0.6 Zr.sub.0.4 Mn.sub.1.5 Cu.sub.0.5                                                     4.917   8.072 178                                        M    Ti.sub.0.6 Zr.sub.0.4 Mn.sub.1.0 Cu.sub.1.0                                                     4.938   8.118 118                                        N    Ti.sub.0.7 Zr.sub.0.3 Mn.sub.1.5 Cu.sub.0.5                                                     4.901   8.040 163                                        O    Ti.sub.0.9 Zr.sub.0.1 Mn.sub.1.5 Cu.sub.0.5                                                     4.855   7.945 33                                         P    Ti.sub.0.6 Zr.sub.0.4 Mn.sub.1.9 Cu.sub.0.1                                                     4.895   8.041 207                                        Q    Ti.sub.0.7 Zr.sub.0.3 Mn.sub.1.7 Cu.sub.0.3                                                     4.883   7.987 149                                        R    Ti.sub.0.6 Zr.sub.0.4 Mn.sub.1.5 Fe.sub.0.5                                                     4.898   8.021 24                                         S    Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.5 Mo.sub.0.5                                                     4.954   8.152 186                                        T    Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.8 Mo.sub.0.2                                                     4.917   8.059 202                                        U    Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.7 Mo.sub.0.3                                                     4.926   8.052 195                                        ______________________________________                                    

As seen in Table 2, when in an atmosphere of hydrogen under high pressure at room temperature, the hydrogen storage material of the invention absorbs large quantities of hydrogen. This absorption moreover is effected easily and in a short time, as shown by test results noted below, and the process is easily reversible to cause release of large amounts of hydrogen.

The invention is described in further detail below with reference to several specific examples thereof.

As a first Example of the hydrogen storage material of the invention there was prepared an alloy in which the base material was TiMn₂ and in which partial substitution of the titanium by zirconium was effected to give alloys having the general formula Ti₁₋α Zr.sub.α Mn₂.0, wherein 0<α<1.

A suitable method for the manufacture of such alloys is as follows. There is prepared a bar of 99% pure titanium, such as commercially available, having a diameter of approximately 8 mm and a length of approximately 10 mm, commercially available 99% pure sponge zirconium, and a plate of 99% pure electrolytic manganese about 1.5 mm thick and 10 mm square. Alloys having the desired formula Ti₁₋α Zr.sub.α Mn₂.0 are formed in a short time if these materials are melted together in an argon arc furnace. To form the hydride, in each case the alloy, is introduced into a pressure-resistant reaction vessel, from which gas is then evacuated. After this, if 99.99% pure hydrogen gas is introduced into the reaction vessel, the reaction vessel is sealed, and the pressure of hydrogen gas therein is brought to and held at approximately 10 atmospheres, absorption of hydrogen by the Ti₁₋α Zr.sub.α Mn₂.0 alloy proceeds rapidly at room temperature, and in a short time there is formed a hydride of the alloy, having for example the composition Ti₀.6 Zr₀.4 Mn₂.0 H₂.5, constituting a metal hydride in which hydrogen is stored. If the pressure of hydrogen gas around the hydride thus formed in the reaction vessel is reduced or if the ambient temperature is increased, hydrogen is released from the alloy and is again available as gaseous hydrogen.

Table 3 shows values, obtained by X-ray diffraction analysis, of the crystal lattice parameters a and c in various alloys having a composition of the general formula Ti₁₋α Zr.sub.α Mn₂.0 and also shows results of measurements of the hydriding characteristics of these alloys indicating the amount of hydrogen absorbed at room temperature and the hydrogen release ratio, i.e., the proportion, expressed as a percentage, of the amount of hydrogen released to the atmosphere at room temperature to the amount of hydrogen absorbed by the alloy as a result of the hydriding process.

The equilibrium diagram of an xTi -- yZr -- zMn alloy is shown in FIG. 2, in which the letters a -- n indicate the correspondingly identified alloys of Table 3, and the shaded portion indicates the range of composition of compounds which offer particular advantages with respect to use thereof as hydrogen storage material.

From FIG. 2 it is seen that in this range the atomic percentage of titanium is 0<x≦60, that of zirconium is 0<y≦60, and that of manganese is z = 40 ˜ 70, with x + y = 30 ˜ 60 and x + y + z = 100.

                  Table 3                                                          ______________________________________                                                          Hydrogen                                                                       Absorption                                                                     (20° C.)                                                                      No. of         Hydro-                                                Crystal   hydrogen       gen                                                   Lattice   atoms/         Release                                  Alloy        Parameters                                                                               No. of         Ratio                                    Code Composition a (A)  a (A)                                                                               alloy atoms                                                                            cc/g (%)                                  ______________________________________                                         a    ZrMn.sub.2.0                                                                               5.040  8.274                                                                               1.2     215  6.7                                  b    Ti.sub.0.2 Zr.sub.0.8 Mn.sub.2                                                             5.001  8.226                                                                               1.18    222  11.0                                 c    Ti.sub.0.4 Zr.sub.0.6 Mn.sub.2                                                             4.967  8.174                                                                               1.15    225  7.6                                  d    Ti.sub.0.5 Zr.sub.0.5 Mn.sub.2                                                             4.946  8.130                                                                               1.12    226  8.0                                  e    Ti.sub.0.6 Zr.sub.0.4 Mn.sub.2                                                             4.903  8.040                                                                               0.82    169  13.4                                 f    Ti.sub.0.7 Zr.sub.0.3 Mn.sub.2                                                             4.878  8.032                                                                               0.58    122  30.8                                 g    Ti.sub.0.8 Zr.sub.0.2 Mn.sub.2                                                             4.861  7.952                                                                               0.03    7.2  35.0                                 h    TiMn.sub.2.0                                                                               4.818  7.902                                                                               0.04    8.2  33.0                                 i    TiMn.sub.1.0                                                                               4.915  8.030                                                                               1.2     283  39.0                                 j    Ti.sub.0.8 Zr.sub.0.2 Mn                                                                   4.962  8.166                                                                               1.22    262  5.3                                  k    Ti.sub.0.9 Zr.sub.0.1 Mn                                                                   --     --   1.26    283  6.3                                  l    TiMn.sub.1.28                                                                              4.888  8.009                                                                               0.91    216  56.0                                 m    Ti.sub.0.8 Zr.sub.0.2 Mn.sub. 1.2                                                          --     --   1.19    259  5.9                                  n    ZrMn.sub.1.0                                                                               --     --   1.47    240  3.8                                  ______________________________________                                    

As seen from Table 3, in an alloy having the composition xTi -- yZr -- zMn if either the proportion x of titanium in terms of atomic percentage or the proportion y of zirconium exceeds 60, or if the sum of x and y is lower than 30 or higher than 60, either the amount of hydrogen absorption becomes extremely small or the amount of hydrogen released at room temperature becomes extremely small. Also, if x or y is higher than 60 or x + y is outside the range 30-60, higher temperature (around 200° C. or more) and high pressure (of the order of 40 atmospheres or more) are necessary to effect absorption of hydrogen. On the other hand, if the atomic percentage of manganese is outside the range 40 ˜ 70, hydrogenation at room temperature is difficult to effect. In addition, if the values of x, y, and z. are outside the ranges noted in reference to FIG. 2, it is difficult to obtain alloys of even quality and insure maintenance of good hydrogen storage characteristics. It was therefore concluded that for this particular type of alloy the values of x, y, and z should be kept within the above-noted ranges.

If such an alloy is represented by a formula indicating proportions of the different components in terms of atomic ratios, for example by the formula Ti.sub.α Zr.sub.β Mn.sub.γ, instead of by the formula xTi -- yZr -- zMn indicating atomic percentages, the corresponding ranges are 0<α≦1.5, 0 <β≦1.5 γ= 0.66 ˜ 2.4, and α+ β = 0.42 ˜ 1.5.

FIG. 3 plots hydrogen dissociation pressure -- composition isotherms for the system Ti₀.5 Zr₀.5 Mn₂.0 -- H. From the drawing it is seen that even for alloy phases for which the amount of released hydrogen is small (18 cc/g) at room temperature, the hydrogen release ratio can be increased considerably by raising ambient temperature to the moderately high value of 124° C.

FIGS. 4 and 5 show the relation between the initial absorption of hydrogen at room temperature by an alloy having the general formula Ti₁₋α Zr.sub.α Mn₂.0 and the crystal lattice parameters a and c, respectively, when the alloy has an MgZn₂ crystal structure and exists as a Laves phase. From Table 3 and FIGS. 4 and 5 it is seen that the amount of hydrogen absorption at room temperature varies with varying values of the parameters a and c, and that for a Ti₁₋α Zr.sub.α Mn₂.0 alloy the most suitable values of the parameters if the alloys are to be employed as hydrogen storage material are in the approximate ranges:

    a = 4.84 ˜ 4.96 (A)

    c = 7.95 ˜ 8.16 (A).

Also it is seen that, as for absorption of hydrogen, release of hydrogen in conditions of normal temperature and pressure is dependent on the crystal lattice parameters a and c of MgZn₂ type crystals constituting a Laves phase.

From the above therefore it is ascertained that the above-described Ti₁₋α Zr.sub.α Mn₂.0 alloys have an MgZn₂ type (C14) crystal structure defining a Laves phase, and that those alloys of this type which have crystal lattice parameters in the above-noted ranges constitute first-rate hydrogen storage materials which can easily absorb and store large amounts of hydrogen at normal temperatures in the vicinity of 20° C.

According to a second embodiment of the invention, there is employed as a base alloy one having the formula Ti.sub.α Mn₂, α being in the range 1.0 ˜ 1.5, and substitution of a portion of the Ti component by zirconium and substitution of a portion of the Mn component by molybdenum are effected, to give an alloy having the general formula Ti_(x-y) Zr_(y) Mn_(2-z) Mo_(z). Hydriding characteristics of this material are described below with reference to Table 4, which notes various examples of alloys having this composition together with the values of the Laves phase MgZn₂ crystal structure parameters thereof.

                                      Table 4                                      __________________________________________________________________________                                             Qty. released                                                    Hydrogen absorption                                                                          hydrogen                                                 Delay   (room temp.)  (room temp.)                                                                             Crystal                                        to initial       H.sub.2 (cc)                                                                             H.sub.2 (cc)                                                                        lattice                      Alloy       Hydriding                                                                            hydrogenation                                                                          at. h    Alloy wt.                                                                           Release                                                                             Alloy wt.                                                                           parameters                   Ti.sub.x-y Zr hd yMn.sub.2-z Mo.sub.z                                                      temp. (min.)  Ti.sub.x-y Zr.sub.y Mn.sub.2-z Mo.sub.z                                                 (g)  ratio (%)                                                                           (g)  a (A)                                                                             c (A)                     __________________________________________________________________________     TiMn.sub.2  24    120     0.11     8.2  33   2.7  4.82                                                                              7.90                      Ti.sub.0.9 Zr.sub.0.1 Mn.sub.1.9 Mo.sub.0.1                                                17    4.5     0.16     11    --  --   4.88                                                                              7.99                      Ti.sub.0.9 Zr.sub.0.1 Mn.sub.1.8 Mo.sub.0.2                                                20    1.6     0.29     21   --   --   4.89                                                                              8.03                      Ti.sub.0.9 Zr.sub.0.1 Mn.sub.1.7 Mo.sub.0.3                                                20    0.5     1.0      70        9.8  6.9                                                                            -- --                                    80    0       0.81     56   8.0  4.4                                           20    0.1     3.1      218  65   143   4.90                                                                             8.05                      Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.9 Mo.sub.0.1                                                49    0       3.0      208  82   171                                           ,0    0.4     3.0      209  67   141                               Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.8 Mo.sub.0.2                                                20    0.3     2.9      202  73   147  4.92                                                                              8.06                                  65    0       2.6      180  84   152                                           20    0       2.9      195  86   167                               Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.7 Mo.sub.0.3       4.93                                                                              8.05                                  56    0       2.1      143  85   121                                           17    0       2.6      167  37   62                                Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.5 Mo.sub.0.5       4.93                                                                              8.10                                  84    0       2.0      128  40   51                                            20    0       2.8      162  7.5  12                                Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.0 Mo.sub.1.0       4.99                                                                              8.23                                  84    0       2.5      146  15   22                                            17    0       3.2      216  37   79                                Ti.sub.0.7 Zr.sub.0.3 Mn.sub.1.9 Mo.sub.0.1       4.96                                                                              7.91                                  50    0       3.1      210  88   184                                           17    0       3.3      217  47   103                               Ti.sub.0.7 Zr.sub.0.3 Mn .sub.1.8 Mo.sub.0.2      4.94                                                                              8.14                                  50    0       3.2      211  83   176                                           17    0       3.3      212  33   69                                Ti.sub.0.7 Zr.sub.0.3 Mn.sub.1.7 Mo.sub.0.3       4.96                                                                              8.14                      ZrMn.sub.2.0                                                                               20    0       3.6      215  6.7  14   5.04                                                                              8.2                       __________________________________________________________________________

As seen from Table 4, requisite ranges of the crystal structure parameters a and c to give suitably good qualities to metallic hydrogen storage material are a = 4.85 ˜ 4.96 (A) and c = 7.95 ˜ 8.18 (A), and optimum hydriding characteristics, especially with respect to release of hydrogen, are achieved by a composition in which the atomic ratios x, y, and z are in the regions of x = 1.0, y = 0.2, and z = 0.3 at room temperature, and x = 1.0, y = 0.3, and z = 0.1 at about 50° C., while release ratios are 86% (167 cc/g) and 88% (184 cc/g) respectively.

To illustrate qualities of examples of alloys of the formula Ti_(x-y) Zr_(y) Mn_(2-z) Mo_(z), the relation between release of hydrogen (cc/g) at room temperature and the value of y when x = 1.0 and z = 0.1 is shown in FIG. 6, and the relation between the amount of released hydrogen (cc/g) and the value of z when x = 1.0 and y = 0.2 is shown in FIG. 7.

Comparing Table 4 and FIGS. 6 and 7, it is seen that in the composition range in which a Ti_(x-y) Zr_(y) Mn_(2-z) Mo_(z) can effectively exist as a Laves phase having an MgZn₂ crystal structure optimum qualities for hydrogen storage material are achieved when the atomic ratios x, y, and z have the value or are in the ranges x = 1.0, y = 0.2 ˜ 0.3, z = 0.1 ˜ 0.4, and that with alloys having such a composition not only is absorption of large amounts of hydrogen possible but also more than 80% desorption hydrogen is easily achieved at a temperature of several tens of degrees centigrade.

Hydrogen dissociation equilibrium -- composition isotherms for the system Ti₀.8 Zr₀.2 Mn₁.7 Mo₀.3 are shown in FIG. 8, and similar curves for the system Ti₀.7 Zr₀.3 Mn₁.9 Mo₀.1 -- H are shown in FIG. 9.

According to a third embodiment of the invention, there is similarly employed as base alloy Ti.sub.α Mn₂.0, α being in the range 1.0 ˜ 1.5, and substitution of a portion of the Ti component by zirconium and of a portion of the Mn component by copper is effected to give an alloy having a composition represented by the general formula Ti_(x-y) Zr_(y) Mn_(2-z) Cu_(z).

The hydriding characteristics of various examples of such an alloy are indicated in Table 5 together with the corresponding a and c of the Laves phase MgZn₂ type crystal lattices defined thereby.

                                      Table 5                                      __________________________________________________________________________                                             Qty. release                                                     Hydrogen abosrption                                                                          hydrogen                                                 Delay   (room temp.)  (room temp.)                                                                             crystal                                  hydrogen-                                                                            to initial       H.sub.2 (cc)                                                                             H.sub.2 (cc)                                                                        lattice                      Alloy       ation hydrogenation                                                                          at.H     alloy wt.                                                                           Release                                                                             Alloy wt.                                                                           parameters                   Ti.sub.x-y Zr.sub.y Mn.sub.2-z Cu.sub.z                                                    temp. (min.)                                                                              Ti.sub.x-y Zr.sub.y Mn.sub.2-z Cu.sub.z                                                    (g)  ratio                                                                               (g)  a (A)                                                                             c (A)                     __________________________________________________________________________     Ti.sub.0.9 Zr.sub.0.1 Mn.sub.1.5 Cu.sub.0.5                                                 0    90      0.40     29   --   --                                                                                  4.85                                                                              7.94                                  20    90      0.46     33   17   5.7                                            0    15      0.29     21   55   11                                Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.7 Cu.sub.0.3       4.86                                                                              7.96                                  20    13      0.29     21   17   3.6                                            0    10      2.0      143  68   98                                Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.5 Cu.sub.0.5       4.89                                                                              8.03                                  20    8       2.0      139  86   120                                            0    30      1.5      102  77   78                                Ti.sub.0.8 Zr.sub.0.2 Mn.sub.1.0 Cu.sub.1.0       4.89                                                                              8.03                                  20    30      1.5      103  75   77                                Ti.sub.0.7 Zr.sub.0.3 Mn.sub.1.9 Cu.sub.0.1                                                17    3       2.0      138  80   111  4.90                                                                              8.05                                   0    3       2.2      153  22   33                                Ti.sub.0.7 Zr.sub.0.3 Mn.sub.1.7 Cu.sub.0.3                                                20    3       2.1      149  41   61   4.88                                                                              7.99                                  47    0       2.1      144  83   119                                           20    1       2.4      163  44   72                                Ti.sub.0.7 Zr.sub.0.3 Mn.sub.1.5 Cu.sub.0.5       4.90                                                                              8.04                                  60    0       2.2      150  85   127                                           20    1       3.0      207  18   36                                Ti.sub.0.6 Zr.sub.0.4 Mn.sub.1.9 Cu.sub.0.1       4.89                                                                              8.04                                  65    0       3.0      204  86   176                               Ti.sub.0.6 Zr.sub.0.4 Mn.sub.1.7 Cu.sub.0.3                                                20    2       3.0      206  13   26                                                                                  4.90                                                                              7.99                                  68    0       2.9      195  85   166                                           20    2       2.7      178  21   38                                Ti.sub.0.6 Zr.sub.0.4 Mn.sub.1.5 Cu.sub.0.5                                                                                      -- --                                    59    1       2.4      162  69   111                                           20    3       1.8      118  13   16                                Ti.sub. 0.6 Zr.sub.0.4 Mn.sub.1.0 Cu.sub.1.0      -- --                                    86    1       1.7      109  56   61                                            20    70      1.5      93   14   13                                Ti.sub.0.6 Zr.sub.0.4 Mn.sub.0.5 Cu.sub.1.5       -- --                                    65    30      1.4      87   19   17                                            19    1       3.3      220  10   22                                Ti.sub.0.5 Zr.sub.0.5 Mn.sub.1.95 Cu.sub.0.05                                              50    0       3.2      212  42   88   4.95                                                                              8.16                                  95    0       3.0      203  80   161                                           14    1       3.3      215  8.2  18                                Ti.sub.0.5 Zr.sub.0.5 Mn.sub.1.9 Cu.sub.0.1       4.94                                                                              8.15                                  95    0       3.2      206  79   163                                           17    3       3.2      207  7.9  16                                Ti.sub.0.5 Zr.sub.0.5 Mn.sub.1.7 Cu.sub.0.3                                                50    2       3.1      202  18   37   4.96                                                                              8.13                                  92    1       3.0      195  80   155                                           14    0       3.5      220  7.0  15                                Ti.sub.0.4 Zr.sub.0.6 Mn.sub.1.9 Cu.sub.0.1       -- --                                    97    0       3.1      196  61   119                                           17    2       3.7      225  6.6  15                                Ti.sub.0.2 Zr.sub.0.8 Mn.sub.1.9 Cu.sub.0.1       5.01                                                                              8.26                                  97    1       3.5      215  10   22                                __________________________________________________________________________

From Table 5 it is seen that optimum qualities for hydrogen storage are achieved by an alloy of the above-noted formula when the crystal lattice parameters a and c are in the ranges a = 4.85 ˜ 4.96 (A) and c = 7.95 ˜ 8.18 (A). It is also seen that optimum hydriding characteristics, particularly with respect to the amount of released hydrogen, are achieved at room temperature when the atomic ratios x, y, and z are respectively in the region of 1.0, 0.2, and 0.5, which values result in a composition which achieves a hydrogen release ratio of 86% (120 cc/g), and in the vicinity of 65° C. when the atomic ratios are respectively about 1.0, 0.4, and 0.1, which values result in a composition which achieves a hydrogen release ratio of 86% (176 cc/g) at this latter temperature.

In illustration of properties of alloys having the general formula Ti_(x-y) Zr_(y) Mn_(2-z) Cu_(z), FIG. 10 plots the relation between the value of y in this formula and the amount of released hydrogen (cc/g) at 60° C. when x = 1.0 and z = 0.1, and FIG. 11 plots the relation between the value of z and the amount of released hydrogen (cc/g) when x = 1.0 and y = 0.3.

Comparison of Table 5 and FIGS. 10 and 11 shows that in the range in which a Ti_(x-y) Zr_(y) Mn_(2-z) Cu_(z) alloy can exist as a Laves phase MgZn₂ type alloy optimum qualities as hydrogen storage material are achieved when the atomic ratios x, y, and z are of the value or in the ranges x = 1.0, y = 0.2 ˜ 0.6, and z = 0.05 ˜ 0.5, and that by employment of alloys having such a composition, it is possible to achieve absorption of a large amount of hydrogen and more than 80% desorption of absorbed hydrogen even when ambient temperature is of the order of only several tens of degrees centigrade.

In further illustration of such an alloy hydrogen dissociation equilibrium -- composition isotherms for the system Ti₀.6 Zr₀.4 Mn₁.9 Cu₀.1 -- H are plotted in FIG. 12.

To resume the above description of various embodiments of the invention, principal conditions for achievement of good characteristics as a hydrogen storage material by an alloy having an MgZn₂ crystal structure and existing as a Laves phase are that the crystal lattices be within the ranges specified in a portion of the claims of the invention, that the alloy phase be uniform and that the alloy components crystallize well, and also that the component elements of the alloy be such that the heat of formation of a hydride by the alloy is of the order of several Kcal/mol H and is comparable to the heat of dissolution of hydrogen from the hydride.

From the above it is concluded that apart from the specific non-limiting examples of the invention described above, the same excellent results may be achieved by suitable combinations of other MgZn₂ type Laves phase alloys constituted by elements of Group IVa or Groups VIa ˜ VIII of the periodic table, for example ZrMn₂, NbMn₂, TiFe₂, ZrV₂ or ZrCr₂.

Although the present invention has fully been described in conjunction with the preferred embodiments thereof with reference to the accompanying drawings, it is to be noted that various changes and modifications are apparent to those skilled in the art.

Accordingly, such changes and modifications are to be understood as included within the true scope of the present invention unless they depart therefrom. 

What is claimed is:
 1. A Ti-Zr-Mn ternary alloy which is substantially a Laves phase intermetallic compound having a hexagonal MgZn₂ (C14) type crystal structure with crystal structure parameters a and c which have values in the range:

    a = 4.80 ˜ 5.10 A,

    c = 7.88 ˜ 8.28 A.


2. An alloy according to claim 1 having the formula xTi -- yZr -- zMn, in which x, y and z are values indicating atomic percentages, 0 21 x ≦ 60, 0 < y ≦ 60, z = 40 ˜ 70, x + y = 30 ˜ 60, and x + y + z =
 100. 3. An alloy according to claim 2 wherein said value of atomic percentage z is approximately equal to 66.7.
 4. An alloy as claimed in claim 1 wherein said crystal lattice parameters a and c are in the range:

    a = 4.84 ˜ 4.96 A

    c = 7.95 ˜ 8.16 A.


5. A Ti-Zr-Mn-Mo quaternary alloy which is substantially a Laves phase intermetallic compound having a hexagonal MgZn₂ (C14) type crystal structure with crystal structure parameters a and c which have values in the range:

    a = 4.80 ˜ 5.10 A,

c = 7.88 ˜ 8.28 A.
 6. An alloy according to claim 5 having the formula Ti_(x-y) Zr_(y) Mn_(2-z) Mo_(z), in which x, y, and z are values indicating atomic ratios, x = 1.0 ˜ 1.5, 0 - y ≦ 1.0, and 0 < z ≦ 1.0.
 7. An alloy according to claim 6, wherein said atomic ratio value x is equal to 1.0.
 8. An alloy according to claim 6, wherein said atomic ratio values x, y, and z are substantially x = 1.0, y = 0.2 ˜ 0.3, and z = 0.1 ˜ 0.4.
 9. An alloy according to claim 8, wherein said atomic ratio values y and z substantially have the values 0.3 and 0.1, respectively.
 10. An alloy according to claim 8, wherein said atomic ratio values y and z substantially have the values 0.2 and 0.3, respectively.
 11. An alloy according to claim 5, wherein said crystal lattice parameters a and c are in the range:

    a = 4.85 ˜ 4.96 A

    c = 7.95 ˜ 8.18 A.


12. A Ti-Zr-Mn-Cu quaternary alloy which is substantially a Laves phase intermetallic compound having a hexagonal MgZn₂ (C14) type crystal structure with crystal structure parameters a and c which have values in the range:

    a = 4.80 ˜ 5.10 A,

    c = 7.88 ˜ 8.28 A.


13. An alloy according to claim 12 having the formula Ti_(x-y) Zr_(y) Mn_(2-z) Cu_(z), in which x, y, and z are values indicating atomic ratios, x = 1.0 ˜ 1.5, 0 < y ≦ 1.0, and 0 < z ≦ 1.5.
 14. An alloy according to claim 13 wherein said atomic ratio value x substantially has the value 1.0.
 15. An alloy according to claim 13 wherein said atomic ratio values are substantially x = 1.0, y = 0.2 ˜ 0.6, and z = 0.05 ˜ 0.5.
 16. An alloy according to claim 15 wherein said atomic ratio values y and z are substantially equal to 0.2 and 0.5, respectively.
 17. An alloy according to claim 15 wherein said atomic ratio values y and z are substantially equal to 0.4 and 0.1, respectively.
 18. An alloy according to claim 12 wherein said crystal lattic parameters a and c are in the range:

    a = 4.85 ˜ 4.96 A

    c = 7.95 ˜ 8.18 A. 